天然海砂已经成为我国部分沿海城市建筑用砂的重要来源,但因其较高的氯含量和夹杂细碎贝壳等特性,在工程应用中受到了一定的限制.本文比照分析了不同氯含量天然海、河砂混凝土的工作性、抗压强度以及抗氯离子渗透性能,探讨了掺合料与耐蚀剂对于内掺型富氯海砂混凝土的适用性与可行性.研究结果表明,混凝土的坍落度随砂中氯含量的增大而显著减小;砂中氯含量大小以及一定掺量掺合料与耐蚀剂的加入,基本不影响混凝土的抗压强度;掺合料与耐蚀剂还可改善混凝土的工作性及抗氯离子渗透性能,18％掺量的耐蚀剂与30％掺量的掺合料对提升混凝土抗氯离子渗透性能的能效相近.
参考文献
| [1] | 水利部长江水利委员会.长江中下游干流河道采砂规划综述[J].人民长江,2003(06):1-4. |
| [2] | 曹雪晴,谭启新,张勇,姜玉池,原晓军.中国近海建筑砂矿床特征[J].岩石矿物学杂志,2007(02):164-170. |
| [3] | Chapman G P;Roeder A R .The effect of sea shells in concrete aggregates[J].Concrete,1970,4(2):71-79. |
| [4] | 楼敦祥 .贝壳砂中贝壳对混凝土性能影响研究[J].宁波高等专科学校学报,1995,1(2):83-87. |
| [5] | Fraj A B;Miraoui M;Boinski F .Early age and durability properties of dredged marine sand mortars[J].ACI Special Publication,2012,289SP:437-451. |
| [6] | 董必钦,刘伟,马红岩,邢锋.海砂砂浆水化过程的电化学阻抗谱研究[J].建筑材料学报,2013(02):306-309,320. |
| [7] | Chandrakeerthy D S R.Suitability of sea sand as a fine aggregate for concrete production[A].Sri Lanka,1994:93-114. |
| [8] | Limeira J;Etxeberria M;Agullo L et al.Mechanical and durability properties of concrete made with dredged marine sand[J].Construction and Building Materials,2011,25:4165-4174. |
| [9] | Dias W P S;Seneviratne G A P S N G;Nanayakkara S M A .Off shore sand for reinforced[J].Construction and Building Materials,2008,22(7):1377-1384. |
| [10] | 洪定海.混凝土中钢筋的腐蚀与保护[M].北京:中国铁道出版社,1998 |
| [11] | 洪乃丰.海砂腐蚀与"海砂屋"危害[J].工业建筑,2004(11):65-67. |
| [12] | 交通部第一航务工程局.海砂中氯盐允许含量问题的探讨[J].施工技术,1979(4):8-14. |
| [13] | 山崎宽司;曾瑞玉.对于在日本使用海砂作为混凝土骨科的看法[J].水利水运科技情报,1995(3):117-122. |
| [14] | O.Lupan;T.Pauporté;I.M.Tiginyanu et al.Comparative study of hydrothermal treatment and thermal annealing effects on the properties of electrodeposited micro-columnar ZnO thin films[J].THIN SOLID FILMS,2011,519:7738-7749. |
| [15] | Arslan M H;Korkmaz H H .What is to be learned from damage and failure of reinforced concrete structures during recent earthquakes in Turkey[J].ENGINEERING FAILURE ANALYSIS,2007,14(1):1-22. |
| [16] | (I)smail H.Cag atay .Experimental evaluation of buildings damaged in recent earthquakes in Turkey[J].ENGINEERING FAILURE ANALYSIS,2005,12(3):440-452. |
| [17] | Ozaki S,Matsuya M .Sixty-year old concrete in a marine environment[J].Transactions of theJapan Concrete Institute,1986,8:169-174. |
| [18] | 洪乃丰 .海砂的利用与钢筋锈蚀的防护[J].建筑技术,1996,1(23):46-49. |
| [19] | 郭成举.氯盐对于水泥水化的促进作用[J].混凝土,1984(5):1-6. |
| [20] | 吴中伟;廉慧珍.高性能混凝土[M].北京:中国铁道出版社,1999 |
| [21] | 王复生,朱元娜,马金龙,孙瑞莲.氯化钠对掺磨细矿渣粉硅酸盐水泥基材料活性激发能力和结合方式影响的试验研究[J].硅酸盐通报,2009(04):784-791. |
| [22] | 刘伟,谢友均,董必钦,邢锋.海砂特性及海砂混凝土力学性能的研究[J].硅酸盐通报,2014(01):15-22. |
| [23] | 王信刚,马保国,胡明玉.水泥基材料的微观结构与离子传输性能[J].材料科学与工程学报,2009(06):880-884. |
| [24] | 陈胡星,马先伟,陈柏连.含粉煤灰或矿渣水泥石的孔结构[J].材料科学与工程学报,2003(03):360-363. |
| [25] | 龙广成,邢锋,余志武,谢友均.自然扩散条件下SO42-、Cl-在砂浆中的沉积特性[J].材料科学与工程学报,2008(05):679-683. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%